ST-WELD Type	Flux	Typical chemical composition %	Hardness	Microstructure	Machinability	Main properties and typical application(TA)
ST-WELD611-S	ST-SF20	C：0.80～1.00  Si：0.50～0.90 Mn：0.80～1.50  Fe:42.00～47.00 else：3.00～4.00  Ni：rest	200～250HB	Austenite	☆☆☆☆	Deposited metal is Fe-Ni alloy,especially for welding and repairing of cast iron with large size
ST-WELD612-O	————	C：1.40～1.70  Si：0.80～1.30 Mn：3.50～4.50  Fe:42.00～47.00 else：2.00～3.50  Ni：rest	170～210HB	Austenite	☆☆☆☆	Deposited metal is Fe-Ni alloy,for welding of grey and ductile cast iron,welding between cast irons or cast iron-steel .No need for preheating .Long and narrow weld is required.
ST-WELD613-G	————	C：0.20～0.40  Si：0.10～0.50 Mn：9.50～10.50  Fe:42.00～47.00 else：2.00～3.50  Ni：rest	170～210HB	Austenite	☆☆☆☆	Deposited metal is Fe-Ni alloy with Mn,for the welding  between cast irons or cast iron-steel . TA:welding and repairing of cast iron,welding between flange steel and cast iron pipe
ST-WELD631-O	————	C：2.00～3.50  Si：2.50～4.50 Mn：0.10～0.50  else：7.00～8.50	180～220HB	ductile cast iron	☆☆☆☆	Deposited metal is ductile cast iron,,for the hot welding  of many kind of cast irons. Preheating temperature and interlayer temperature must be higher than 450℃.